Rotec® ABS 1001 FR V0/5
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0EDpZt_Rotec-ABS-1001-FR-V0-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rotec®ABS 1001 FR V0/5 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main features of ABS 1001 FR V0/5 are:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 47 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 91.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | < 235 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Slow |
| Injection instructions |
|---|
| Screw rotation speed: slowBack pressure: 10%Injection pressure: high |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 170 - 200 | °C | |
| Cylinder Zone 2 Temp. | 170 - 200 | °C | |
| Cylinder Zone 3 Temp. | 170 - 200 | °C | |
| Cylinder Zone 4 Temp. | 170 - 200 | °C | |
| Cylinder Zone 5 Temp. | 170 - 200 | °C | |
| Melt Temperature | < 200 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3825 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Mirathane™ L95 | Miracll Chemicals Co., Ltd. | TPU-Capro | Mirathane™ |
| TAROMID A 280 H G9 DX0 TR1 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Wellamid® 22LHI4 XE-GY1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| ADENE NHJAGD | A.D. Compound spa | PP Copolymer | ADENE |