LNP™ THERMOCOMP™ RC006XXC compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0A4p0w_LNP-THERMOCOMP-RC006XXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* RC006XXC is a compound based on Nylon 66 containing Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound PDX-R-84487 Product reorder name: RC006XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.32 | % | |
| Across Flow : 24 hr | 0.97 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.55 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.78 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 23600 | MPa | ASTM D638 |
| -- | 23100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 267 | MPa | ASTM D638 |
| Break | 259 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 19300 | MPa | ASTM D790 |
| -- 5 | 19300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 358 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 376 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 99 | J/m | ASTM D256 |
| 23°C 7 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 980 | J/m | ASTM D4812 |
| 23°C 8 | 58 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.40 | J | ASTM D3763 |
| -- | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 262 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 257 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 248 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILOY® 200A | Samyang Corporation | PC+ABS | TRILOY® |
| KPOL-PP K-PPC 6.0 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |
| Hostacom G3 N01 102297 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Jam PE 235F7 | Jam Petrochemical Company | LLDPE | Jam PE |
| LNP™ THERMOCOMP™ MFB22S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |