PENTAMID A CV10 H black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 09magg_PENTAMIDACV10Hblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, 10% carbon fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.50 | % | ISO 294-4 |
| Flow | 0.35 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 7.8 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.6 | % | ISO 62 |
| Viscosity Number | 140 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 34 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 240 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA66, MHRC, 14-90 N, CF10 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.13 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 265 - 290 | °C | |
| Middle Temperature | 275 - 300 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 78.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANCEED® mL216 | Lotte Chemical Titan (M) Sdn. Bhd. | LLDPE | TITANCEED® |
| KumhoSunny PBT 3735FG | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |
| Karina CLEAR PVC COMPOUND -E 80/266-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| O'Tech OW 649 AFR | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Plexiglas® Satinice df22 7N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |