Jamplast JPPCGP
| Category: | PC , Polycarbonate |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 09GWi9_Jamplast-JPPCGP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
JPPCGP series resins are general purpose PC that exhibit an excellent physical property balance of heat resistance, and impact strength. This product can be supplied with a mold release packaga, a UV stabilizer package or both. This product is typically used for appliances, storage media housings, extruded sheet, electrical components and lighting. Available Melt Flow Rates: 4, 6, 10, 15 |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2300 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 72.4 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus 4 | 2410 | MPa | ASTM D790 |
| Flexural Strength 5 | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 910 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 142 | °C | |
| 1.8 MPa, Unannealed | 122 | °C | |
| 1.8 MPa, Annealed | 139 | °C | |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.0 to 91.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 271 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 299 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 76.7 to 110 | °C | |
| Screw Speed | 40 to 70 | rpm | |
| Clamp Tonnage | 2.8 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 15.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1004-625UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Spectrum S640 | Spartech Plastics | HDPE | Spectrum |
| Bergadur™ PB40 G20 BK009 | PolyOne Corporation | PBT | Bergadur™ |
| GERMAMID 6 GF 30 HSZ | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| SQUARE® LIM1510-45A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |