Order Products : sales@su-jiao.com
Jam 22501KJ
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Jam Petrochemical Company |
| Trademark: | Jam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 07sryp_Jam22501KJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
22501 is a LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. this resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications. Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.95 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness | 15.0 - 150 | µm |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm, blown film | 200 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm, blown film | 240 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 13.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 12.5 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 45.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 680 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 780 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 110 | g | ASTM D1922 |
| TD : 25 µm, blown film | 460 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 38 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 21 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M30053S | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Sylvin 7833-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EVERLON® TSO-75 | Ever Polymer Co., Ltd. | SEBS+EPDM | EVERLON® |
| Kepamid® 1500ST | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Sylvin 5145-70 CLEAR RED 6192 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |