SABIC® LDPE PCG00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 07n8xp_SABIC-LDPE-PCG00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG00 is an additive-free grade produced using SABIC's proprietary high pressure Clean Tubular Reactor (CTR®) which typically ensures grades with high purity. It is typically used for semi-rigid containers obtained by Blow Fill Seal (BFS) process and medical films. Compliance to Regulations SABIC® LDPE PCG00 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.33 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 220 | MPa | |
| TD | 220 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 12.0 | MPa | |
| TD : Yield | 12.0 | MPa | |
| MD : Break | 28.0 | MPa | |
| TD : Break | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | > 200 | % | |
| TD : Break | > 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | 250 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 20 | g | Internal Method |
| Re-blocking | < 5.0 | g | Internal Method |
| Tear Strength | ISO 6383-2 | ||
| MD | 35.0 | kN/m | |
| TD | 45.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ISO 306/A |
| Melting Temperature (DSC) | 114 | °C | DIN 53765 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 57 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® E3400 SP | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Ferro PP LPP40BC15NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 7844-90C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8027-65 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALFATER XL® A90E 2GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |