Polytron® A35B01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 04Sx18_Polytron-A35B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% LONG FIBER GLASS REINFORCED BLACK NYLON 6.6 HEAT STABILIZED FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.30 | % | ASTM D955 |
| -- | 0.20 to 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | 3.4 | % | ASTM D570 |
| Saturation, 23°C | 3.4 | % | ISO 62 |
| Equilibrium | 1.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 180 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 280 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C | 21 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman ABS 780 | Shuman Plastics, Inc. | ABS | Shuman ABS |
| TAISOX 8001 | Formosa Plastics Corporation | HDPE | TAISOX |
| ALFATER XL® A90I 3EF0001 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Globalene® 8181 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| LNP™ THERMOCOMP™ RZ006S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |