INEOS LLDPE LL6910LA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 02Plcg_INEOS-LLDPE-LL6910LA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6910LA is rigid blown film grade offering a certified low level of gels making it ideal for lamination or thin film applications with highly decorative printing. Benefits and Features LL6910LA is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer which offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.936 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) 1(190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 450 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, Blown Film | 18.0 | MPa | |
| TD : Yield, 38 µm, Blown Film | 21.0 | MPa | |
| MD : 38 µm, Blown Film | 54.0 | MPa | |
| TD : 38 µm, Blown Film | 36.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 38 µm, Blown Film | 780 | % | |
| TD : Break, 38 µm, Blown Film | 990 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 65 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 35 | g | |
| TD : 25 µm, Blown Film | 330 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Condition 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® FN727 NC010A | DuPont Performance Polymers | Nylon 6 | Zytel® |
| BCC Resins BC 7053 | BCC Products Inc. | Epoxy | BCC Resins |
| Anjatech® 250-T2/GF30 | Almaak International GmbH | Nylon 6 | Anjatech® |
| Chemlon® 109-14 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| DOWLEX™ 2038.68G | The Dow Chemical Company | LLDPE | DOWLEX™ |