Plexiglas® LED 8N LD48

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	01cqxt_Plexiglas-LED-8N-LD48.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PLEXIGLAS® LED 8N LD48 is a highly transparent light guide material based on PLEXIGLAS® 8N.
In addition to the typical properties of PLEXIGLAS®, such as

Excellent weather resistance

UV-stability

Good flow, high mechanical strength

PLEXIGLAS® LED 8N LD48 is developed for edge lit LED applications. The light scattering properties convert the light guide to a full illuminated panel. Furthermore, the material allows for a competely transparent view through the light guide when it is not illuminated. This opens a new degree of freedom for designers.
PLEXIGLAS® LED 8N LD48 is recommended for panels with a distance of up to 24 cm to 48 cm between two light injecting LED strips.

Application:
Preferably, for injection molding, but can also be used for special extrusion.

Examples:
BLU (Back lighting) for LCD-Displays, illuminated freeform panels, ambient lighting, illuminated handle bars and switches. Illuminated outline contours for devices.

Processing:
PLEXIGLAS® LED 8N LD48 can be processed on injection molding machines with 3-zone general purpose screws for engineering thermoplastics.

General Information
Features	Good Flow Good Weather Resistance High Clarity High Strength Light Stabilized
Uses	Optical Applications
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	3.00	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Stress (Break)	77.0	MPa	ISO 527-2/5
Tensile Strain (Break)	5.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	103	°C	ISO 75-2/B
1.8 MPa, Unannealed	98.0	°C	ISO 75-2/A
Glass Transition Temperature	117	°C	ISO 11357
Vicat Softening Temperature	108	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2
Haze	< 2.0	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	< 98.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	60.0 to 90.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Maxelast® D6785	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
4PROP® 9D12430 FR5HUV	4Plas	PP Homopolymer	4PROP®
DAI-EL™ G-751	DAIKIN AMERICA, INC.	Fluorelastomer	DAI-EL™
Di-Pak™ E-4595-3	Hapco Inc.	TP, Unspecified	Di-Pak™
Lumid® SG2460B	LG Chem Ltd.	Nylon 66	Lumid®